UT Muitilayer CAD/CAM Zirconia Block
Seamless gradients of chroma and translucency mimic the vitality of natural dentition resulting in a simplified, time-saving workflow.
UT Muitilayer CAD/CAM Zirconia Block
Safety: Good biocompatibility 丨CAM - Nesting friendly 丨Transition - No Layer lines
HT/ST/SHT/UT/3D/4D-ML Sintering
Max Heating rate:10°℃ per minute
Final temperature:1500℃-1550℃，1530°℃ is best
Holding time at final temperature:130min
Cooling should be done without temperature control in closde furnace
Never open the furnace before it has reached a temperature of less than 80°℃ to avoid thermal shocks
| Product Type | Translucency | Strength | Colors | Sintering Temperature |
| 4D-Pro Multilayer | 43-57% | 700-1000MPa | White,16 VITA,BL1-4 | 1530℃ |
| 3D-Pro Multilayer | 43-55% | 800-1200MPa | White,16 VITA,BL1-4 | 1530℃ |
| SHT-C | 49% | 900MPa | White,A1,A2,A3,B1,B2 | 1530℃ |
| SHT-ML | 49% | 900MPa | A1,A2,A3,B1,B2,BL1-4 | 1530℃ |
| ST | 43% | 1200Mpa | White,16 VITA | 1530℃ |
| ST-ML | 43% | 1200MPa | 16 VITA | 1530℃ |
| UT | 57% | 600MPa | White,16 VITA | 1530℃ |
| UT-ML | 57% | 600MPa | 16 VITA | 1530℃ |
| HT | 40% | 1350MPa | White | 1530℃ |
Zirconia material is an excellent high-tech biomaterial with good biocompatibility and superior to various metal alloys, including gold. Zirconia teeth have no irritation and no allergic reaction to the gums, so it is suitable for use in the oral cavity, avoiding allergic, irritation, corrosion and other adverse reactions caused by metals in the oral cavity.